Volatilization loss of Al element can be decreased by increasing melting temperature and shorten holding time.
采用X荧光光谱(XRF)分析水冷铜坩埚真空感应炉熔炼(ISM)加入和不加入稀土Y的Ti 22Al 25Nb合金铸锭成分,分析结果表明,在保证获得成分均匀的合金铸锭的情况下,Al的挥发烧损在28。